- layer thickness 2-10 mm (15 mm for small areas)
- faster Strength (technological movement on a surface already through 6-7 hours)
- high strength - not less than 15 MPa
- it spreads well and gives a smooth surface.
- high adhesion to substrates
- does not shrink
Packing: 25 kg
Certified product in accordance with ISO 14024, environmental certificate No. UA.08.002.440more details
Self-leveling mix for floors PSV-015 – ready dry mix for leveling and repair of small roughnesses of floors, practically all types of hydrophilic bases, resistant to deformation (cement, concrete, expanded concrete and other) with a layer from 2 to 10 mm (15 mm for small sections) residential or industrial buildings. Gives a flat, smooth, solid horizontal surface for laying out various coverings (parquet, laminate, carpet, linoleum, tile, etc.).
If there is a need to increase the elasticity, hydrophobic properties, as well as the adhesion of the solution to the base – to prepare the solution with the addition of concentrated emulsions: contact PL-125 and elastic PL-127.
If necessary, the alignment in the systems of heated floors to prepare the solution with the addition of elastic emulsion PL-127.
There are no reviews yet.
|Structure||mixture of cement, gypsum mineral fillers and organic additives|
|Appearance||homogeneous granular mixture gray without impurities|
|aggregate size||no more than 0.63 mm|
|mixing ratio||~ 4.5-5.0 l of water per 25 kg (~ 0.19 + 0.01 liters of water to 1 kg) of dry mixture, depending on the desired consistency|
|spreadability||at least 20 cm|
|Thickness||2-10 mm (and 15 mm for small areas)|
|Temperature of the substrate and bases||+10 to +25 ° C|
|Shelf life after mixing||at least 20 minutes|
|Time of possible technological movement||6-7 hours|
|Adhesion to the substrate||not less than 0.5 MPa|
|Shrinkage mortar||not more than 2.0 mm / m|
|Performing further work||not earlier than 48 hours|
|The compressive strength (after 3 days)||not less than 5.0 MPa|
|Compression strength (after 28 days)||not less than 15.0 MPa|
|Tensile strength in bending (after 28 days)||not less than 3.0 MPa|
|Operating temperature of the solidified solution||from +1 to +45 ° C at a relative humidity less than 90%|
|Consumption of dry mixture||~ 1.7-1.8 kg / m² at 1 mm layer thickness|
Select site language:
ПОЛІПЛАСТ ™ ОГОЛОШУЄ КОНКУРС НА ЧЕСТЬ ДНЯ БУДІВЕЛЬНИКА
◾ Суперприз🏆 – крутезний лазерний лінійний нівелір (лазерний рівень)
◾ Комплект брендованого професійного одягу👷♂️(комбенізон, футболка, бейсболка)
◾ Корисна сувенірна продукція для будівельника🧰