Properties:
- for machine and manual application
- adapted to all types of plastering stations
- PCSH-018 M - cement-limestone with the addition of perlite
- PCSh-018 ML - lightweight cement-limestone, with increased perlite content
- especially recommended for porous foundations (gas and foam concrete blocks, ceramic blocks and bricks)
- high vapor permeability
- layer thickness: 8-25 mm per application
- for internal and external works
- plastic and easy to use
- base color: white, gray
Packing: 25 kg
- Application
- Specifications
- Features
- Reviews
Plasters PCSH-018 M / PCSH-018 ML are universal modified cement-lime plaster mixtures with the addition of perlite, recommended for machine and manual application and adapted to all types of plastering stations. Intended for plastering walls and ceilings from foam and aerated concrete blocks, brick and concrete surfaces for further decoration with decorative plasters, paints or tiling. They are especially effective when plastering surfaces made of aerated concrete. They are used inside and outside buildings. The hardened solution has high vapor permeability.
PCSH-018 ML is a professional formula with increased perlite content. Improves the thermal insulation properties of the enclosing structure. It has high technical and operational characteristics. Recommended for facades.
There are no reviews yet.
| PСSh-018 M | PСSh-018 ML | ||
| Composition | cement-lime mixture with mineral fillers and modifying additives, contains perlite | ||
| Appearance | homogenous free-flowing mixture without foreign impurities | ||
| Color | off-white or off-white | ||
| mixing ratio | 0.19 l ± 0.01 l of water per 1 kg of dry mixture; 4.5 – 5.0 liters of water per 25 kg of dry mix | 0.21 l ± 0.01 l of water per 1 kg of dry mixture; 5.0 – 5.5 liters of water per 25 kg of dry mix | |
| Aggregate size | no more than 0.63 mm | ||
| Shelf life from start of mixing | at least 60 minutes | ||
| Air and substrate temperature during application | from +5°С to +30°С | ||
| Layer thickness | 8-25 mm per application layer | 8-20 mm per application layer | |
| Mobility | at least 8 cm | ||
| Adhesion to the substrate | not less than 0.2 MPa | ||
| Compressive strength after 28 days | not less than 2.5 MPa | not less than 4.0 MPa | |
| Flexibility after 28 days | not less than 1.2 MPa | not less than 1.5 MPa | |
| Vapor permeability of the solution | not less than 0.1 mg/m*hour*Pa | ||
| Thermal conductivity | no more than 0.3 W/(m*K) | ||
| Frost resistance | at least 50 cycles | ||
| Operating temperature of the hardened solution | from -30°С to +70°С | ||
| Dry mix consumption | 1.15-1.2 kg/m2 /mm layer thickness | 1.1 kg/m2 /mm layer thickness | |