Highly adhesive plaster Cement spray
- Strengthens and roughens the base
- Improves adhesion of the plaster coating to the substrate
- Equalizes the absorbency of the substrate
- Moisture resistant and vapor permeable
- Frost resistant
- For manual and mechanized application
- For outdoor and indoor use
Packing: 25 kg
The polymer-cement mixture PСSh-007 (spray) is designed to create a cement spray on the surfaces of wall structures in order to improve the adhesion strength of subsequent plaster coatings to the base and equalize its absorbency.
Mineral substrates can be processed: cement-lime, cement-sand, concrete and brick; as well as wood substrates such as fiberboard, fixed formwork, etc.
PСSh-007 is effective for the installation of reinforced layers for plastering or tiling.
! For manual and machine application.
There are no reviews yet.
|Composition||mixture of cement with mineral fillers and modifiers|
|Appearance||homogeneous free-flowing mixture without impurities|
|Mixing ratio||4.5 – 5.0 liters per 25 kg of dry mix|
~ 0.19 l ± 0.01 l of water per 1 kg of dry mix
|Aggregate size||no more than 0.8 mm|
|Expiry date from the beginning of mixing||not less than 60 minutes|
|Application layer thickness||up to 5 mm|
|Mobility||not less than 8.0 cm|
|Air and substrate temperature during application||from + 5 ° С to + 30 ° С|
|Mixing water temperature||from +15 ° С to +20 ° С|
|Substrate adhesion||not less than 0.8 MPa|
|Compressive strength after 28 days||not less than 15 MPa|
|Frost resistance||at least 50 cycles|
|Operating temperature of the hardened mortar||from -30 ° С to +70 ° С|
|Dry mix consumption||from 1.7 kg / m2 per 1 mm of application layer thickness|