tech description
PSV-045
Mixtures for the installation of floor elements
Radiation Test Report | PSV-045
Properties:
- contains quartz fillers
- high strength of 50 MPa
- high resistance to the influence of minor and medium mechanical loads
- high resistance to abrasion
- for internal and external works
Packing: 25 kg
Application
- Application
- Specifications
- Features
- Reviews
Strengthening polymer cement coating-topping for industrial floors PSV-045 gives the concrete base resistance to abrasion, impact resistance, high surface strength and density, reduces the adsorption of oils and fats. The PSV-045 mixture is used to strengthen the top layer of concrete floors that are subjected to minor and medium mechanical loads during operation (warehouses, trade halls, workshops, light industry premises, etc.).
There are no reviews yet.
Сomposition | high-activity portland cement, fractionated quartz aggregates and modifier additives |
Appearance | homogeneous mass of granular gray without impurities |
The maximum size of the placeholder | not more than 4.0 mm |
Moisture content | not more than 0,5% |
Temperature range of use | from +10 ° C to +30 ° C |
Readiness of the floor for technological loads | after 7 days |
Readiness of the floor for operation | after 28 days |
Operating temperature of the floor | from -50 °С tо +70 °С |
Consumption of dry mixture | 4-5 kg / m² |
The compressive strength at the age of 3 days | not less than 20 MPa |
The ultimate compressive strength at the age of 28 days | not less than 60 MPa |
The tensile strength of bending at the age of 28 days | not less than 7.0 MPa |
Strength of adhesion to a concrete base after keeping in air-dry conditions | not less than 1.5 MPa |
Erasure | not more than 0.7 g / cm2 |
Shrinking | not more than 1.5 mm / m |
Frost resistance | at least 75 cycles |