High-strength reinforced floor screed
- Repair of floors and alignment of horizontal surfaces, surfaces at an incline
- increased crack resistance
- inside and outside buildings
- optimal for heated floors, "floating" floors
- reinforced with polyamide fiber
- plasticThe thickness of the layer is 10-100mm
- high strength, moisture resistant, frost resistant
- high adhesion to the base
- easy to level, plastic
Packing: 25 kg
Certified product in accordance with ISO 14024, environmental certificate No. UA.08.002.440more details
High-strength reinforced flooring screed PSP-031 is a dry construction modified mix reinforced with polyamide fiber. Used inside dry or wet rooms and outside buildings to perform screeds, slope screed, leveling and repair of strong hydrophilic substrates resistant to deformation (cement, concrete, expanded concrete, etc.) before application of leveling mixtures, laying tiles, parquet, laminate, linoleum and other decorative coatings.
Gives a flat, smooth, solid horizontal surface. Due to its high fiber content and optimum particle size distribution, it has high strength and increased fracture toughness, so it can be used in various construction schemes (floating-type floors, “warm” floors, etc.).
Moisture-resistant, frost-resistant, plastic, resistant to shrinkage, high adhesion to the base, strength not less than 25 MPa, layer thickness from 10 to 100mm.
If there is a need to increase the elasticity, hydrophobic properties or adhesion of the solution to the base – the solution mixture should be prepared using concentrated emulsions TM Polyplast: contact PL-125, elastic PL-127.
There are no reviews yet.
|Structure||cement mixture with mineral fillers and polymeric modifiers|
|Appearance||homogeneous granular mixture gray without impurities|
|Fraction||not more than 1.25 mm|
|mixing ratio||~ 3.0-3.5 l of water per 25 kg (0,13 ± 0,01 liter of water for 1 kg) of dry mixture, depending on the desired consistency|
|Temperature of the substrate and bases||+5 to +30 ° C|
|Shelf life after mixing||at least 60 minutes|
|The layer thickness per pass||10-100 mm|
|Adhesion to the substrate||not less than 0.5 MPa|
|Compression strength (after 28 days)||not less than 25.0 MPa|
|Tensile strength in bending (after 28 days)||not less than 4.5 MPa|
|Shrinkage (after 28 days)||not more than 1.0 mm / m|
|Performing further work||not earlier than 48 hours|
|Operating temperature of the solidified solution||-30 to +70 ° C.|
|Consumption of dry mixture||~ 1.8-2.1 kg / m² at 1 mm layer thickness|
Select site language:
ПОЛІПЛАСТ ™ ОГОЛОШУЄ КОНКУРС НА ЧЕСТЬ ДНЯ БУДІВЕЛЬНИКА
◾ Суперприз🏆 – крутезний лазерний лінійний нівелір (лазерний рівень)
◾ Комплект брендованого професійного одягу👷♂️(комбенізон, футболка, бейсболка)
◾ Корисна сувенірна продукція для будівельника🧰