Adhesive mixture fast-curing universal
Adhesive mixture PP-022 EXPRESS is a modified construction mix for use in conditions that require quick work, on horizontal and vertical bases resistant to deformations (concrete, cement, cement-lime, brick, plasterboard, etc).
Building a system of bonded facade insulation (based on mineral wool or polystyrene foam insulation) in difficult weather conditions: spring, autumn.
A mixture of PP-022 EXPRESS is used for bonding insulation plates, and for the device of a protective reinforced layer;
Fixing tiles with low water absorption (less than 1%), as well as tiles and tiles of large sizes, porcelain tiles (tiles “GRES”), ceramic and glass-ceramic tiles, tiles from natural (except marble **) and artificial stone and similar materials, as well as fixing tiles using the “tile to tile” method.
In the systems “warm floor” with water and electric heating.
It is used both inside and outside the buildings.
The glue mixture can be used both as an independent mortar and as an additive to the mortar to improve its technical characteristics.
If necessary, to increase the hydrophobic properties, as well as adhesion to the base, to prepare the adhesive mixture using the contact concentrate PL-125 or the elastic emulsion PL-127 TM Poliplast®.
For fastening of plates, tiles and mosaics from natural stone of white color or transparent rocks, glue PP-015 or PP-016 TM Poliplast® is used.
There are no reviews yet.
|Composition||mix of cement with mineral aggregates and polymer modifiers|
|Appearance||homogeneous granular mixture of gray color without impurities|
|Filler size||no more than 0.8 mm|
|Mixing ratio||~ 0.19 ± 0.01 l of water per 1 kg of dry mix|
|Temperature of the substrate and bases when applied||from -5 to +30 °С|
|Expiration date from the moment of mixing||at least 30 minutes|
|Open time||at least 10 minutes|
|The mobility of the mixture||7±2 cm|
|Time of possible technological movement:||not earlier than 3 hours|
not earlier than 6 hours
|Adhesion strength with the base after aging in air-dry conditions||no more than 0.5 MPa|
|Adhesion to the base after alternate freezing and thawing, 50 cycles||no more than 0.5 MPa|
|Operating temperature of the hardened solution||from -30 to +70 °С|
|Frost-resistance||At least 50 cycles|
|Water absorption coefficient||Not more than 0.6 kg/m2/hour|
|Shrinkage||Not more than 1.5 mm/m|
|Dry mix consumption||for gluing insulation – 5.0 – 8.0 kg/m²|
for the device of the protective layer in the heat insulation system – 3.0 – 8.0 kg/m²
for tiling – from 1.5-1.6 kg/m² layer thickness