Heat-resistant mixture for stoves and fireplaces
- fastening of ceramic tile and natural stone with water absorption not less than 1%
- moisture resistantFor surfaces subjected to intense heat loads (surfaces of furnaces, fireplaces, heated floors)
- for exterior and interior work, dry and damp areas
- high heat resistance (up to 170ºC)
- high adhesion and fixing ability
- frost resistant
Packing: 20 kg
Heat-resistant adhesive mixture PP-018 HotFIX is a ready-made dry adhesive mixture used for fastening ceramic tiles, tiles, natural stone tiles, clinker, terracotta tiles, majolica and other similar facing materials with a water absorption of at least 1% and dimensions of no more than 400x400mm on surfaces of furnaces, fireplaces and other horizontal and vertical foundations resistant to deformation (concrete, cement-sand, brick, etc.), intended for operation under the influence of elevated temperatures (up to +170°C) and cyclical effects.
It is used both indoors and outdoors.
It is not used for lining the hearths of furnaces and fireplaces.
There are no reviews yet.
|Compound||mixture of cement with mineral fillers and polymer modifiers|
|Appearance||homogenous free-flowing mixture without foreign impurities|
|Color||Shaded gray (white on request)|
|Mixing ratio||4.0 – 4.4 liters of water per 20 kg (0.21 ± 0.01 liters of water per 1 kg) of dry mix|
|Aggregate size||no more than 0.63 mm|
|Shelf life from start of mixing||at least 120 minutes|
|open time||at least 30 minutes|
|Adjustment time||at least 10 minutes|
|Air and substrate temperature during application||from +5 to +30 °С|
|The thickness of the adhesive layer under the tile||no more than 10 mm|
|Tile offset (for vertical surfaces)||no more than 0.5 mm|
|Adhesion strength to the base in air-dry conditions (after 28 days)||not less than 1.3 MPa|
|Adhesion strength with the base after soaking in water is||not less than 1.0 MPa|
|Adhesion strength to the base after heat aging (70 °C)||not less than 1.0 MPa|
|Adhesion strength to the substrate after freeze and thaw cycles||not less than 1.0 MPa|
|Compressive strength (after 28 days)||not less than 10 MPa|
|Frost resistance||at least 50 cycles|
|Operating temperature of the hardened solution||from -30 to +170°C|
|Time of possible technological movement (sewing)||not earlier than 48 hours|
|Dry mix consumption||from 2 kg/m2 (average 1.5 – 1.8 kg/m2/mm)|