PСSh-009

Reinforced polymer-cement plaster

high-strength
crack resistant
reinforced with microfibers
easy to apply up to 20 mm
for leveling concrete bases of swimming pool bowls, retaining walls, ceilings, facades, plinths
for manual and machine application
for interior and exterior work

Polymer-cement reinforced plaster PCSh-009 – a dry cement-based building mixture intended for:

repair and leveling of existing plastered surfaces;
plastering and leveling of walls and ceilings made of concrete, brick, foam and gas blocks, cement-sand bases;
leveling of weathered monolithic retaining walls, building facades;
leveling of concrete bases of swimming pool bowls before applying waterproofing and cladding.
Due to the high polymer content, it is effective in thin-layer application, repairing small cracks, depressions and other defects. Forms a strong base for subsequent decoration with all types of tiles (ceramic, stoneware, large-format, concrete and others) with natural stone, applying waterproofing, decorative plasters, gluing decorative elements, puttying, painting, etc. For use inside and outside buildings in thicknesses from 2 to 20 mm in one application. When mixed with water, it forms a workable solution that is easy to apply both manually and by machine.

Do not use for floor repairs.

There are no reviews yet.

Structure	cement mixture with mineral fillers and polymeric modifiers
Appearance	homogeneous granular mixture gray without impurities
aggregate size	not more than 0.8 mm
Temperature of the substrate and a base	+ 5 ° C to + 30 ° C
mixing ratio	4.75 – 5.25 l of water per 25 kg of dry mixture (0.20+/-0.01 l per 1 kg of dry mixture)
Shelf life after mixing	at least 60 minutes
Mobility mortar	at least 6cm
Adhesion to the substrate	~ 0.5 MPa
Compressive strength after 28 days	not less than 13 MPa
Tensile strength in bending	not less than 4.0 MPa
water vapor permeability	at least 0.05 mg / m × h × Pa
crack resistance	absence of cracks in the layer of 20 mm thickness
frost-resistance	not less than 50 cycles
Operating temperature of the solidified solution	from -50 ° C to + 70 ° C
frost-resistance	not less than 50 cycles
Consumption of dry mixture	~ 1.6 kg / m² at 1 mm layer thickness