Two-component epoxy waterproof high strength joint filler
- for outdoor work
- frost resistant, crack resistant, weatherproof
- available in three colors
- color resistance to aggressive atmospheric environment
- resistant to grass overgrowing
- high strength (not less than 45 MPa)
Packing: comp. A - 25 l + comp. B - 5 l
High-strength waterproof joint filler PDR-074 is designed to fill joints with a width of 10 mm or more in clinker pavers (paving bricks), polygon stone or curly paving elements (FEMs) made of concrete and natural stone, the operation of which is designed for exposure to atmospheric factors and constant passage heavy transport.
High-strength joint filler PDR-074 is intended for joint use with a draining underlying layer PDR-070 (PDR-070 +), a waterproofing layer PRG-01 (PRG-02) and chute elements for water drainage when covering urban areas, streets of historic cities, carriageway of roads, parking lots, cargo areas, etc.
The PDR-074 mortar is resistant to efflorescence and damage caused by exposure to low temperatures, and is also resistant to the formation of cracks in wide joints and is intended for use on surfaces exposed to any operational loads.
! Available in three colors: gray, black, beige.
There are no reviews yet.
|Structure||сomponent A: a mixture of cement with mineral aggregates and polymer modifiers, сomponent B: epoxy resin|
|Color||gray, black, beige|
|Mixing ratio||component A = 25 kg : component B = 4.55 kg|
|Size of filler||up to 2 mm|
|The term mortar suitability||~ 35 minutes|
|Layer thickness||from 30 mm; when loading from transport – from 40 mm; when applied to a separate layer – from 50 mm|
|The width of the seams||from 10 mm (depth of not less than 30 mm); of 15 mm (depth 2 times the width of the seams)|
|Compressive strength (after 7 days)||not less than 45 MPa|
|Tensile strength in bending (after 7 days)||not less than 20 MPa|
|Adhesion to the substrate||not less than 0.5 MPa|
|Frost-resistance||not less than 75 cycles|
|Time of possible technological movement||not earlier than 48 hours, after complete curing of the bedding layer at 23 ° C and humidity level at|
|The ability to perceive the load||light load – after 7 days; staff load – after 14 days|
|Consumption||6-17 kg / m² depending on the depth and width of the seams|